I materiali
Scegliete tra un'ampia gamma di polveri di alta qualità che offrono prestazioni e durata superiori.
Rame
Caratteristiche del materiale
Superior yield strength, improved machinability.
Applicazioni
Busbars, cable clamps, electrical connectors, heatsinks, moulds, and anti-microbial coatings.
| Elemento | Percentuale |
|---|---|
| Cu, min | 99.70% |
| Oxygen, max | 0.15% |
| CAST (riferimento) | SPEE3D STAMPATO | ||
| Standard | CC040A spec3 | Pure Copper as heat treated and annealed4 | |
| Resistenza allo snervamento (MPa) | ASTM E82 | 40 | XY = 115 (min)
Z = 110 (min) |
| Resistenza alla trazione finale (MPa) | ASTM E82 | 150 | XY = 180 (min)
Z = 175 (min) |
| Elongation at break (min %) | ASTM E82 | 25 | XY = 9 (min)
Z = 8.5 (min) |
| Hardness (min HV5) | ASTM E18 | 40 | 60 (typ) |
| Electrical Conductivity (%IACS) | ISO15548-1 | 86-98 | 95 (typ) |
| Thermal Conductivity | W/m.K | 372 | 380 (typ) |
- Properties shown reflect beta processing parameters. Properties were obtained for annealing loads between 0.2 kg and 3 kg.
- Campioni testati secondo la norma ASTM E8.
- From standard EN 1982:2008.
- Material heat treated and annealed according to SPEE3D SOP standard operating procedure.
- Value calculated from electrical conductivity.
Le denominazioni elencate sono solo a scopo di riferimento. La composizione e le proprietà meccaniche possono variare. Le prestazioni del materiale per uso finale sono influenzate (+/-) da alcuni fattori, tra cui, ma non solo, la geometria e la progettazione del pezzo, l'applicazione e le condizioni di valutazione.